Products > Resin Systems at Technology Marketing > Fire Retardant Epoxies
  PT2475 A/B PT5355 A/B or B1 PT5358 A/B
Color Off-White White White
Mix Ratio, By Weight 100 : 13 100 : 19 100 : 14
Mixed Viscosity, cps 2,100 - 2,300 cps 900 - 1,000 cps 4,000 - 5,000 cps
Pot Life, @ 77°F 60 - 65 min Part B - 30 min.
Part B1 - 1 hour		 40 min.
Cured Hardness, Shore D 87 Shore D 88 Shore D 85 Shore D
Specific Gravity, gms./cc 1.23 1.19 1.24
Tensile Strength, psi 26,492 psi 45,775 psi 45,775 psi
Elongation @ Break, % 1.57 % 1.50 % 1.50 %
Tensile modulus, psi 2,353,522 psi 2,754,557 psi 2,754,557 psi
Flexural Strength, psi 59,980 psi 59,437 psi 59,437 psi
Flexural Modulus, psi 2,501,855 psi 2,894,587 psi 2,894,587 psi
Compressive Strength, psi 13,626 psi 11,265 psi 13,245 psi
Compressive Modulus, psi 526,053 psi 455,294 psi 525,458 psi
GO TO BULLETIN PT2475 PT5355 PT5358